Nanopartículas Magnéticas de óxido de Hierro como matrices de liberación controlada

Abstract

In this paper is carried out preparation of magnetites by different methods, co-precipitation and solvothermal, and its subsequent coating with mesoporous silica. Also, have been characterized using various characterization techniques: XRD, FT-IR, adsorption-desorption of N2 at - 196 °C, SEM and magnetization curves. The results obtained indicate that the best method is the solvothermal since it allows to obtain uniform nanoparticles, small size with spherical morphology and more magnetism, which makes them suitable to be used as matrice of controlled release

En este trabajo se ha llevado a cabo la preparación de magnetitas por distintos métodos, coprecipitación y solvotermal, y su posterior recubrimiento con sílice mesoporosa. Asimismo, se han caracterizado utilizando diferentes técnicas: DRX, FT-IR, Adsorción-desorción de N2 a -196ºC, curvas de magnetización y SEM. Los resultados obtenidos indican que es el método solvotermal el que permite obtener nanopartículas homogéneas, de pequeño tamaño, con morfología esférica y mayor magnetismo, propiedades que las hace idóneas para ser utilizadas como matrices de liberación controlada